PENGARUH VARIASI ARUS PENGELASAN SMAW TERHADAP SIFAT MEKANIK BAJA ST 37 UNTUK RANGKA MESIN PEMOTONG KAYU

PUTRA, MOHAMAD FARIZ PRATAMA (2025) PENGARUH VARIASI ARUS PENGELASAN SMAW TERHADAP SIFAT MEKANIK BAJA ST 37 UNTUK RANGKA MESIN PEMOTONG KAYU. Skripsi thesis, Universitas Pancasakti Tegal.

	Text COVER - BAB III FARIZ (1).pdf Download (1MB)
	Text BAB IV - V FARIZ.pdf Restricted to Repository staff only Download (699kB)
	Text DAFTAR PUSTAKA - LAMPIRAN FARIZ.pdf Download (1MB)

Abstract

MOHAMAD FARIZ PRATAMA PUTRA (2024) “PENGARUH VARIASI ARUS PENGELASAN SMAW TERHADAP SIFAT MEKANIK BAJA ST 37 UNTUK RANGKA MESIN PEMOTONG KAYU”. Skripsi, prodi teknik mesin fakultas teknik dan ilmu komputer Universitas Pancasakti Tegal. Pengelasan didefinisikan sebagai proses pembentukan ikatan metalurgi pada sambungan logam atau paduan logam dengan mencairkan bahan sampai kondisi meleleh atau cair. Metode pengelasan yang umum diterapkan dalam industri konstruksi adalah Shielded Metal Arc Welding (SMAW). Tujuan penelitian ini untuk mengetahui pengaruh variasi arus pada pengelasa terhadap nilai kekuatan tarik, bending dan impact pada baja ST 37. Metode penelitian menggunakan alat: trafo las listrik, grinda potong, sikat baja, palu konde, palu terak. Bahan yang digunakan: baja karbon rendah ST 37, elektroda E-6013 diameter 2,6. Penelitian ini menggunakan metodologi eksperimen dengan memvariasikan variasi arus 70 A, 80 A, 90 A, pada pengelasan baja ST 37. Hasil pengelasan di uji dengan menggunakan pengujian tarik, bending, dan uji impak. Pada hasil pengujian tarik kuat arus 70 amper mempunyai kuat tarik 456,1 Mpa sedangkan pada kuat arus 80 amper mempunyai kuat tarik 456,5 Mpa dan kuat arus 90 amper mempunyai kuat tarik 435,3 Mpa. Disimpulkan untuk kekuatan tarik tertinggi berturut-turut diberikan oleh jenis variasi arus 80 amper, 70 amper, 90 amper. Pada hasil pengujian bending ini untuk arus terbesar pada 80 amper dan arus terendah pada 70 amper pada masing masing arus untuk 80 amper mempunyai lengkungan sebesar 1098,94 Mpa di ikuti arus 90 amper mempunyai nilai sebesar 1040,30 Mpa, dan untuk arus terendah pada 70 amper mempunyai nilai 929,15 Mpa. Hasil dari pengujian impact ini untuk arus terbesar pada 90 amper dan arus terendah pada 80 amper. Pada masing-masing arus memiliki nilai untuk arus 90 amper mempunyai nilai 1,236 J/mm2 nilai terbesar selanjutnya 70 amper 1,179 J/mm2 dan arus terendah pada 80 amper mempunyai nilai 1,116 J/mm2. hasil pengujian tarik, bending, dan impact pada setiap sampel atau spesimen dengan variasi arus 70A, 80A, dan 90A dalam proses pengelasan SMAW menunjukkan bahwa kekuatan tertinggi pada pengujian tarik dan bending terdapat pada sampel dengan variasi arus 80A karena dapat memberikan pengaruh positif terhadap kekuatan tarik, bending, dan impact. Hal ini disebabkan oleh kesesuaian arus 80A dalam menciptakan penguatan antar sambungan yang optimal. Kata kunci : Las SMAW, Baja ST 37, Uji tarik, uji bending, uji impack MOHAMAD FARIZ PRATAMA PUTRA (2024) "THE EFFECT OF VARIATIONS IN SMAW WELDING CURRENT ON THE MECHANICAL PROPERTIES OF ST 37 STEEL FOR WOOD CUTTING MACHINE FRAME". Thesis, mechanical engineering study program, faculty of engineering and computer science, Pancasakti University, Tegal. Welding is defined as the process of forming a metallurgical bond at a metal or metal alloy joint by melting the material until it melts or melts. The welding method commonly applied in the construction industry is Shielded Metal Arc Welding (SMAW). The aim of this research is to determine the effect of tensile, bending and Impak strength values on ST 37 steel. The research method uses tools: electric welding transformer, cutting grinder, steel brush, bun hammer, slag hammer. Materials used: low carbon steel ST 37, electrode E-6013 diameter 2.6. This research uses an experimental methodology by varying current variations of 70 A, 80 A, 90 A. Welding results are tested using tensile, bending and Impak tests. In the tensile test results, a current strength of 70 amperes has a tensile strength of 456.1 Mpa, while a current strength of 80 amperes has a tensile strength of 456.5 Mpa and a current strength of 90 amperes has a tensile strength of 435.3 Mpa. It was concluded that the highest tensile strength was given by the current variations of 80 amperes, 70 amperes, and 90 amperes respectively. In the results of this bending test, the highest current is at 80 amperes and the lowest current is at 70 amperes. Each current for 80 amperes has a bend of 1098.94 Mpa, followed by a current of 90 amperes which has a value of 1040.30 Mpa, and for the lowest current at 70 ampere has a value of 929.15 Mpa. The results of this Impak test are for the largest current at 90 amperes and the lowest current at 80 amperes. For each current, the value for a current of 90 amperes has a value of 1.236 J/mm2, the next largest value is 70 amperes, 1.179 J/mm2 and the lowest current at 80 amperes has a value of 1.116 J/mm2. The results of tensile, bending and Impak tests on each sample or specimen with current variations of 70A, 80A and 90A in the SMAW welding process show that the highest strength in tensile and bending tests is found in samples with current variations of 80A because it can have a positive influence on tensile strength. , bending, and Impak. This is due to the suitability of the 80A current in creating optimal reinforcement between connections. Key words : SMAW welding, ST 37 steel, tensile test, bending test, Impak test

Item Type:	Karya Ilmiah (Skripsi)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik dan Ilmu Komputer > Teknik Mesin
Depositing User:	admin repository upstegal
Date Deposited:	26 Feb 2025 03:56
Last Modified:	26 Feb 2025 03:56
URI:	http://repository.upstegal.ac.id/id/eprint/10195

Actions (login required)

View Item