ANALISIS KEKUATAN TANGKI SEPEDA MOTOR LISTRIK MENGGUNAKAN CAMPURAN SERABUT KELAPA DENGAN RESIN POLYESTER

YASIN, ANGGA PURNAMA NURUL (2025) ANALISIS KEKUATAN TANGKI SEPEDA MOTOR LISTRIK MENGGUNAKAN CAMPURAN SERABUT KELAPA DENGAN RESIN POLYESTER. Skripsi thesis, Universitas Pancasakti Tegal.

	Text COVER - BAB III ANGGA - Angga Purnama N.Y79.docx Download (3MB)
	Text BAB IV - V ANGGA - Angga Purnama N.Y79.docx Restricted to Repository staff only Download (327kB)
	Text DAFTAR PUSTAKA - LAMPIRAN ANGGA - Angga Purnama N.Y79.docx Download (3MB)

Abstract

ANGGA PURNAMA NURUL YASIN (2024) “ANALISIS KEKUATAN TANGKI MOTOR LISTRIK MENGGUNAKAN CAMPURAN SERABUT KELAPA DENGAN RESIN POLYESTER” Skripsi, Prodi Teknik Mesin Fakultas Teknik dan Ilmu Komputer Univesitas Pancasakti Tegal. Material komposit merupakan material gabungan dua atau lebih material yang terikat secara makroskopis. Tujuan penelitian ini untuk mengetahui variasi serabut kelapan dengan resin polyester terhadap nilai kekuatan tarik, bending, impak. Metode penelitian ini menggunakan alat: Cetakan kaca, timbangan digital, kuas, stempet, gerinda tangan, Bahan yang digunakan: Serabut kelapa dan resin polyester. Penelitian ini menggunakan metodologi eksperimen dengan memvariasikan variasi serabut kelapa dengan resin polyester 2%, 4%, 6% pada kekuatan tarik, bending, impak. Hasil pengujian tarik komposit serabut kelapa yang telah dilakukan penelitian tiga jenis variasi serabut kelapa yang berbeda yaitu variasi serabut kelapa 2%, 4%, dan 6%. Dari pengujian tersebut didapatkan hasil bahwa rata-rata tegangan terbesar pada 2% mengalami kenaikan pada kekuatan tarik. Kekuatan tarik tertinggi pada fraksi 2% sebesar 18,7 N/mm2 , sedangkan pada fraksi 4% sebesar 17,0 N/mm2 dan pada fraksi 6% sebesar 13,8 N/mm2, jadi penambahan serabut kelapa berpengaruh terhadap kekuatan tarik,Hasil pengujian bending komposit serabut kelapa yang telah dilakukan penelitian tiga jenis variasi serabut kelapa yang berbeda yaitu variasi serabut kelapa 2%, 4%, dan 6%. Dari pengujian tersebut didapatkan hasil bahwa rata-rata tegangan terbesar pada 2% sebesar 20,49 Mpa jadi penambahan serabut kelapa terhadap kekuatan bending sangat berpengaruh. Kemudian pada fraksi 4% sebesar 15,31 Mpa dan fraksi 6% sebesar 14,58 Mpa, Hasil pengujian impak komposit serabut kelapa yang telah dilakuk. penelitian tiga jenis variasi serabut kelapa yang berbeda yaitu variasi serabut kelapa 2%, 4%, dan 6%. Dari pengujian tersebut didapatkan hasil bahwa rata-rata tegangan terbesar pada 6% sebesar 0,016 J/mm2. sedangkan pada fraksi 4% sebesar 0,013 J/mm2 dan fraksi 2% sebesar 0,012 J/mm2. Dari hasil data tersebut menunjukan bahwa fraksi serat 2% merupakan komposisi yang paling baik dibanding lainnya, dimana dengan fraksi ini akan dapat menguatkan komposit resin polyster. Kata kunci : Tangki motor listrik, komposit, matrik polyester, serabut kelapa, uji tarik, uji bending, dan uji impak.   ABSTRACT ANGGA PURNAMA NURUL YASIN (2024) “ELECTRIC MOTOR TANK STRENGTH ANALYSIS USING A MIXTURE OF COCONUT FIBER WITH POLYESTER RESIN” Thesis, Mechanical Engineering Study Program, Faculty of Engineering and Computer Science, Pancasakti University, Tegal. Composite material is a combined material of two or more materials that are macroscopically bound. The purpose of this study was to determine the variation of eighth fiber with polyester resin on tensile strength, bending, and impact values. This research method uses tools: Glass molds, digital scales, brushes, stamps, hand grinders, Materials used: Coconut fiber and polyester resin. This study uses an experimental methodology by varying the variation of coconut fiber with polyester resin 2%, 4%, 6% on tensile strength, bending, impact. The results of tensile testing of coconut fiber composites that have been studied using three different types of coconut fiber variations, namely coconut fiber variations of 2%, 4%, and 6%. From these tests, it was found that the average largest stress at 2% experienced an increase in tensile strength. The highest tensile strength at 2% fraction was 18.7 N/mm2, while at 4% fraction it was 17.0 N/mm2 and at 6% fraction it was 13.8 N/mm2, so the addition of coconut fibers affected the tensile strength. The results of bending testing of coconut fiber composites that have been studied using three different types of coconut fiber variations, namely coconut fiber variations of 2%, 4%, and 6%. From these tests, it was found that the average largest stress at 2% was 20.49 Mpa, so the addition of coconut fibers to the bending strength was very influential. Then at 4% fraction of 15.31 Mpa and 6% fraction of 14.58 Mpa, The results of the coconut fiber composite impact test that has been carried out. research on three different types of coconut fiber variations, namely coconut fiber variations of 2%, 4%, and 6%. From the test, the results obtained that the average largest stress at 6% was 0.016 J/mm2. while at 4% fraction of 0.013 J/mm2 and 2% fraction of 0.012 J/mm2. The results of the data show that the 2% fiber fraction is the best composition compared to others, where this fraction can strengthen the polyester resin composite. Keywords: Electric motor tank, composite, polyester matrix, coconut fiber, tensile test, bending test, and impact test.

Item Type:	Karya Ilmiah (Skripsi)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik dan Ilmu Komputer > Teknik Mesin
Depositing User:	admin repository upstegal
Date Deposited:	26 Feb 2025 07:13
Last Modified:	26 Feb 2025 07:13
URI:	http://repository.upstegal.ac.id/id/eprint/10208

Actions (login required)

View Item