ANALISIS PENGARUH VARIASI ARUS LAS SMAW TERHADAP KEKUATAN PENGELASAN PADA PERANCANGAN CASIS DINO TEST

Fikih Handrika, Fikih (2020) ANALISIS PENGARUH VARIASI ARUS LAS SMAW TERHADAP KEKUATAN PENGELASAN PADA PERANCANGAN CASIS DINO TEST. Skripsi thesis, Universitas Pancasakti Tegal.

[img] Text
proposal fix benar-2 NEW FIKIH3 (Recovered).pdf
Restricted to Repository staff only

Download (3MB) | Request a copy

Abstract

ABSTRAK Fikih Handrika, Analisis Kekuatan Pengelasan Jenis SMAW pada Perancangan Casis Dyno Test. Skripsi : Program Studi Teknik Mesin Fakultas Teknik Mesin Universitas Pancasakti Tegal 2019. Pemilihan arus pengelasan yang mempengaruhi hasil pengelasan adalah parameter pengelasan, kualitas hasil pengelasan di pengaruhi oleh energi panas yaitu arus las. apabila pemilihan arus las yang kurang tepat maka hasil pengelasan tidak akan teratur, melebar dan tidak rata. penelitian ini bersifat eksperimensuatu cara untuk mencari hubungan sebab akibat antara dua faktor yang saling berpengaruh. Dengan melakukan pemeriksaan dan pengujian hasil las dengan variasi arus pengelasan terhadap sifat-sifat mekanik hasil las pada baja st. 37 dengan menggunakan jenis las SMAW DC 400 G dan memakai jenis elektroda RD diameter 3,2 mm dan E 7016 atau RD LB52U. Pada uji kekerasan terdapat pada spesimen hasil las arus 80 ampere sebesar 179,11% kg/mm² terletak pada daerah logam lasan. Nilainya mengalami kenaikan sebesar 12,42% kg/mm² terhadap nilai kekerasan spesimen hasil las pada kuat arus 60 ampere dan sebesar 205,29% kg/mm² terhadap nilai kekerasan spesimen hasil las pada kuat arus 70 ampere mengalami kenaikan tertinggi dibandingkan untuk spesimen hasil las pada kuat arus 80 ampere. Nilai kekuatan tarik untuk spesimen hasil las pada kuat arus 70 ampere mengalami kenaikan tinggi dengan spesimen 60 ampere sebesar 13,76% kg/mm². Nilai regangan untuk spesimen hasil las pada kuat arus 80 ampere mengalami kenaikan sebesar 6,02% kg/mm² dibandingan dengan raws material dan kuat arus 60 ampere serta 70 ampere. Nilainya mengalami kenaikan sebesar 3,82%kg/mm² terhadap spesimen hasil arus 70 ampere. Kata kunci : Arus Pengelasan, SMAW, Kekerasan, Kekuatan Tarik. ABSTRACT Fikih Handrika,Analysis of the Welding Strength of the SMAW type in the Design of the Dyno Test Chassis. Thesis : Mechanical Faculty of Engineering, University of Pancasakti Tegal. welding currents selection that affects the welding results is the welding parameters, the quality of welding results is influenced by heat energy, namely the welding current. If the welding current selection is not right then the welding results will not be regular, wide and uneven. This research is experimental in a way to find a causal relationship between two factors that influence each other, by checking and testing the results of welding with a variation of the welding current on the mechanical properties of welding results on steel st. 37 by using a SMAW DC 400 G welding type and using a electrodes type RD diameter 3,2 MM and E 7016 or RD LB52U In the hardness Test contained in the 80 amperes current weld specimen of 179,11% kg/mm located in the weld metal area the value has increased by 12,42% kg/mm against the hardness value of the weld specimens at 60 amperes current strength and by 205,29% kg/mm against the hardness of the specimen 60 ampers and the current strength of 70 amperes has the haighest increase compared to the specimen results of welds at 80 amperes current strength. The value of tensile strength for specimens of welding results at 70 amperes of high currenth strength increased with a specimen of 60 amperes as large as 13,76% kg/mm. tenuous values for weld speccimens at 80 ampere of current experienced a hardship of 6,02% kg/mm compared to raws meterial and strong current of 60amperes and 70 amperes. The value has increased by 3,82%kg/mm over the 70 amperes current specimen. Keywords : Welding Current SMAW, Hardness, Tensile Strength

Item Type: Karya Ilmiah (Skripsi)
Uncontrolled Keywords: Arus Pengelasan, SMAW, Kekerasan, Kekuatan Tarik. Welding Current SMAW, Hardness, Tensile Strength
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Fakultas Teknik dan Ilmu Komputer > Teknik Mesin
Depositing User: fikih fikih Fikih Handrika
Date Deposited: 21 Feb 2020 03:11
Last Modified: 10 Jan 2023 02:29
URI: http://repository.upstegal.ac.id/id/eprint/1305

Actions (login required)

View Item View Item