VARIASI MEDIA PENDINGINAN PADA PENGELASAN SMAW PADA BAJA ST37

SAPUTRA, FERY JIRAWAN DION (2025) VARIASI MEDIA PENDINGINAN PADA PENGELASAN SMAW PADA BAJA ST37. Skripsi thesis, Universitas Pancasakti Tegal.

	Text bab 1-3 skripsi fery - Fery Jirawan Dion Saputra (1).docx Download (5MB)
	Text bab 4-5 skripsi fery - Fery Jirawan Dion Saputra.docx Restricted to Repository staff only Download (1MB)
	Text daftar pustaka dan lampiran skripsi fery - Fery Jirawan Dion Saputra.docx Download (38kB)

Abstract

ABSTRAK Fery Jirawan Dion Saputra, 2024 “Variasi Media Pendinginan Pada Pengelasan SMAW Pada Baja ST 37” Skripsi, Jurusan Teknik Mesin Fakultas Teknik dan Ilmu Komputer Universitas Pancasakti Tegal 2024. Dalam dunia industri tentunya sudah tidak asing lagi dengan penggunaan las jenis SMAW atau las busur logam las, dalam penggunaan las SMAW tentunya terdapat beberapa faktor yang dapat mempengaruhi hasil pengelasan contohnya saja seperti pemilihan penggunaan pendinginan. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh dari variasi pendingin air, air coolant, dan air accu terhadap kekuatan tarik, kekuatan lengkung dan kekerasan pengelasan SMAW pada baja ST 37. Metode penelitian yang digunakan dalam penelitian ini adalah metode eksperimen langsung. Penelitian ini menggunakan bahan plat baja ST 37 dengan jenis las yang digunakan adalah las SMAW yang kemudian dilakukan perlakuan pendinginan setelah pengelasan dengan variasi menggunakan media pendinginan air, air coolant, air accu, dan kemudian dilakukan pengujian tarik, pengujian bending, dan pengujian kekerasan. Nilai rata-rata dari pengujian tarik tertinggi pada pendingin air cooland sebesar 461,48 N/mm2, nilai rata-rata tertinggi pada pengujian bending adalah pada pendingin air accu sebesar 65,2 N/mm2 dan pada pengujian kekerasan tertinggi terletak pada pendingin air sebesar 209,77 HB. Kata kunci : Pengelasan SMAW, Pengaruh Media pendingin, Tarik, Lengkung, Kekerasan, Baja ST 37. ABSTRACT Fery Jirawan Dion Saputra, 2024 "Variations of Cooling Media in SMAW Welding on ST 37 Steel" Thesis, Department of Mechanical Engineering, Faculty of Engineering and Computer Science, Pancasakti University, Tegal, 2024. In the industrial world, of course you are already familiar with the use of SMAW welding or metal arc welding. When using SMAW welding, of course there are several factors that can influence the welding results, for example the choice of cooling used. The aim of this research is to determine the effect of variations in water cooling, water coolant and battery water on the tensile strength, bending strength and hardness of SMAW welding on ST 37 steel. The research method used in this research is the direct experimental method. This research uses ST 37 steel plate material with the type of welding used is SMAW welding which is then subjected to cooling treatment after welding with variations using water cooling media, coolant water, battery water, and then tensile testing, bending testing and hardness testing are carried out. The average value of the highest tensile test on the cooland water cooler was 461.48 N/mm2, the highest average value on the bending test was on the battery water cooler of 65.2 N/mm2 and the highest hardness test was on the water cooler of 65.2 N/mm2. 209.77 HB. Keywords: SMAW Welding, Effect of Cooling Media, Tensile, Curvature, Hardness, ST 37 Steel.

Item Type:	Karya Ilmiah (Skripsi)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik dan Ilmu Komputer > Teknik Mesin
Depositing User:	admin repository upstegal
Date Deposited:	19 Feb 2025 04:56
Last Modified:	19 Feb 2025 04:56
URI:	http://repository.upstegal.ac.id/id/eprint/10116

Actions (login required)

View Item