ANALISIS PROSES FLAME HARDENING PADA RODA GIGI DENGAN VARIASI MEDIA PENDINGIN

Abdullah, Muhammad Furqon (2025) ANALISIS PROSES FLAME HARDENING PADA RODA GIGI DENGAN VARIASI MEDIA PENDINGIN. Skripsi thesis, Universitas Pancasakti Tegal.

	Text COVER--BAB 3 - M Furqon (1).docx Download (2MB)
	Text BAB 4 & BAB 5 - M Furqon.docx Restricted to Repository staff only Download (1MB)
	Text DAPUS & LAMPIRAN - M Furqon.docx Download (1MB)

Abstract

Muhammad Furqon Abdullah, 2025 “Analisis Proses Flame Hardening Pada Roda Gigi Dengan Variasi Media Pendingin”. Skripsi, Teknik Mesin Fakultas Teknik Universitas Pancasakti Tegal. Roda gigi merupakan komponen yang sering digunakan pada kendaraan bermotor untuk meningkatkan dan mengatur kecepatan putaran suatu daya dengan memberikan rasio roda gigi tertentu. Bagaimana pengaruh quenching (pendinginan) dengan media air aquades, air coolant, dan air kelapa terhadap pengujian mekanik kekuatan material AISI 304. Baja paduan SS AISI 304 merupakan jenis baja tahan karat austenitic stainless steel yang memiliki komposisi 0.042%C, 1.19%Mn, 0.034%P, 0.006%S, 0.049%Si, 18.24%Cr, 8.15%Ni, dan sisanya Fe. Tujuan penelitian ini agar mengetahui hasil pengujian mekanik dari material AISI 304,mengetahui perbandingan metode pendinginan yang paling tepat untuk pembuatan roda gigi yang kuat. Dengan Metode eksperimen adapun langkah-langkah percobaan yang dilakukan pertama dengan pembuatan spesimen, pemanasan flame hardening, dan pendinginan secara cepat. Bahan yang digunakan adalah baja AISI 304 dengan setiap kelompok mendapatkan proses flame hardening dengan suhu 790 ⁰C selama 30 menit dan didinginkan secara cepat (Quenching). Hasil pengujian sifat mekanik material AISI 304, memiliki nilai kekerasan yang meningkat, dengan variasi pendinginan pada percobaan menggunakan air kelapa memiliki nilai kekerasan sebesar 235,1 BHN sehingga menurunkan kekerasan, Variasi pendinginan dengan air coolant memiliki nilai keausan rata- rata terendah yang dengan nilai 0,000656 mm³/kg.m, hasil dari pengamatan mikro pendinginan dengan air coolant memiliki ukuran kristal yang halus sehingga dapat mengindikasikan material mengalami pendinginan secara konstan dan merata pada material. Kata kunci: AISI 304, roda gigi, Flame hardening, uji kekerasan, uji keausan dan uji micro Muhammad Furqon Abdullah, 2025 "Analysis of Flame Hardening Process on Gears with Variations in Cooling Media". Thesis, Mechanical Engineering, Faculty of Engineering, Pancasakti University, Tegal. Gears are components that are often used in motor vehicles to increase and regulate the rotational speed of a power by providing a certain gear ratio. How does quenching (cooling) with distilled water, coolant water, and coconut water affect the mechanical strength testing of AISI 304 material. SS AISI 304 alloy steel is a type of austenitic stainless steel that has a composition of 0.042% C, 1.19% Mn, 0.034% P, 0.006% S, 0.049% Si, 18.24% Cr, 8.15% Ni, and the rest Fe. The purpose of this study is to determine the results of mechanical testing of AISI 304 material, to determine the comparison of the most appropriate cooling methods for making strong gears. With the experimental method, the experimental steps carried out were first by making specimens, heating flame hardening, and cooling rapidly. The material used was AISI 304 steel with each group getting a flame hardening process with a temperature of 790 ⁰C for 30 minutes and cooled rapidly (Quenching). The results of testing the mechanical properties of AISI 304 material, 304 has an increased hardness value, with variations in cooling in the experiment using coconut water having a hardness value of 235.1 BHN thus reducing the hardness, Variations in cooling with coolant water have the lowest average wear value with a value of 0.000656 mm³/kg.m, the results of micro observations of cooling with quenching water have a fine crystal size so that it can indicate that the material experiences constant and even cooling on the material, Keywords: AISI 304, gears, Flame hardening, hardness test, wear test and micro test.

Item Type:	Karya Ilmiah (Skripsi)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik dan Ilmu Komputer > Teknik Mesin
Depositing User:	admin repository upstegal
Date Deposited:	20 Mar 2025 03:00
Last Modified:	20 Mar 2025 03:00
URI:	http://repository.upstegal.ac.id/id/eprint/10326

Actions (login required)

View Item