SETIAWAN, MOKHAMAD RERA (2025) ANALISA SIFAT MEKANIS CAMPURAN Al DAN SiC PADA PENGECORAN ALUMINIUM. Skripsi thesis, Universitas Pancasakti Tegal.

	Text COVER-BAB 3 - Rhera Setiawan.docx Download (6MB)
	Text BAB 4-5 - Rhera Setiawan.docx Restricted to Repository staff only Download (490kB)
	Text Daftar pustaka dan Lampiran_compressed - Rhera Setiawan.pdf Download (1MB)

Abstract

Mokhamad Rera Setiawan,2025. “Analisa Sifat Mekanis Campuran Al Dan SiC Pada Pengecoran Aluminium ”. Skripsi, Program Studi Teknik Mesin Fakultas Teknik dan Ilmu Komputer Universitas Pancasakti Tegal 2025. Pengecoran logam adalah proses pembuatan coran dimana coran dibuat dari logam cair, dituangkan ke dalam cetakan, kemudian didinginkan hingga memadat. Aluminium adalah logam ringan dengan sifat mekanik,ketahanan korosi, serta hantaran listrik yang baik. Logam ini digunakan untuk tidak hanya untuk peralatan rumah tangga, tetapi juga untuk berbagai keperluan matrial pesawat terbang, kapal, konstruksi dan industri otomotif, dll. Silicon carbide (SiC) adalah jenis material keramik dengan karakteristik yaitu dengan ketahaan mekanik, kimia dan konduktivitas termal baik. Tujuan penelitian ini yaitu untuk mengetahui pengaruh penambahan silicon karbida SiC terhadap kekuatan mekanik hasil pengecoran paduan logam Aluminium. Pada penelitian ini Alumunium yang digunakan adalah limbah piston. Variasi yang digunakan adalah fraksi berat penambahan Silikon Karbida SiC sebesar 3%, 4% dan 5%. Kemudian untuk pengambilan data menggunakan uji sifat fisis meliputi uji sifat mekanik yaitu uji kekerasan, uji tarik dan uji keausan. Selanjutnya menganalisa data dari hasil pengujian. Berdasarkan hasil uji yang diperoleh, nilai kekerasan tertinggi dimiliki hasil pengecoran Alumunium dangan penambahan Silikon Karbida 3% dengan nilai rata rata kekerasan sebesar 68,0 kg/mm2. Nilai kekuatan tarik tertinggi dimiliki hasil pengecoran Alumunium dangan penambahan Silikon Karbida 3% dengan nilai rata rata sebesar 84,1 Mpa. Nilai laju keausan terendah tertinggi dimiliki hasil pengecoran Alumunium dangan penambahan Silikon Karbida 3% dengan nilai rata rata keausan spesifik sebesar 0,001214 mm3/kg.m. Maka dapat disimpulkan bahwa semakin besar penambahan Silikon Karbida maka akan semakin menurun kekuatan mekanik hasil pengecoran paduan logam Alumunium. Kata kunci : pengecoran logam, alumunium, silikon karbide, uji kekerasan, uji tarik, uji keausan. ABSTRAK Mokhamad Rera Setiawan, 2025. “Analysis of the Mechanical Properties of Al and SiC Mixtures in Aluminum Castings ". Thesis, Mechanical Engineering Study Program, Faculty of Engineering and Computer Science, Pancasakti University, Tegal 2025. Metal casting is the process of making castings where the castings are made from molten metal, poured into molds, then cooled until they solidify. Aluminum is a light metal with good mechanical properties, corrosion resistance and electrical conductivity. This metal is used not only for household appliances, but also for various materials for aircraft, ships, construction and automotive industries, etc. Silicon carbide (SiC) is a type of ceramic material with the characteristics of mechanical, chemical resistance and good thermal conductivity. The aim of this research is to determine the effect of adding silicon carbide SiC on the mechanical strength of aluminum alloy castings. In this research, the aluminum used was piston waste. The variation used is the added weight fraction of Silicon Carbide SiC of 3%, 4% and 5%. Then to collect data using physical properties tests including mechanical properties tests, namely hardness tests, tensile tests and wear tests. Next, analyze the data from the test results. Based on the test results obtained, the highest hardness value was obtained from aluminum casting with the addition of 3% Silicon Carbide with an average hardness value of 68.0 kg/mm2. The highest tensile strength value was obtained from aluminum casting with the addition of 3% Silicon Carbide with an average value of 84.1 Mpa. The lowest wear rate value was obtained from aluminum casting with the addition of 3% silicon carbide with an average specific wear value of 0.001214 mm3/kg.m. So it can be concluded that the greater the addition of Silicon Carbide, the more the mechanical strength of the aluminum alloy casting results will decrease. Keywords : metal casting, aluminum, silicon carbide, hardness test, tensile test, wear test.

Item Type:	Karya Ilmiah (Skripsi)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik dan Ilmu Komputer > Teknik Mesin
Depositing User:	admin repository upstegal
Date Deposited:	20 Mar 2025 03:43
Last Modified:	20 Mar 2025 03:43
URI:	http://repository.upstegal.ac.id/id/eprint/10328

Actions (login required)

View Item