ANALISA MATA PISAU MESIN PENCACAH SAMPAH ORGANIK MENGGUNAKAN BAHAN BAJA KARBON ST 41 DENGAN PROSES HEAT TREATMENT BERTINGKAT

JAELANI, MOHAMAD ABDUL (2021) ANALISA MATA PISAU MESIN PENCACAH SAMPAH ORGANIK MENGGUNAKAN BAHAN BAJA KARBON ST 41 DENGAN PROSES HEAT TREATMENT BERTINGKAT. Skripsi thesis, Universitas Pancasakti Tegal.

Text Skripsi Mohamad Abdul Jaelani.pdf Download (4MB)

Abstract

ABSTRAK MOHAMAD ABDUL JAELANI. 2021 “ANALISA MATA PISAU MESIN PENCACAH SAMPAH ORGANIK MENGGUNAKAN BAHAN BAJA KARBON ST 41 DENGAN PROSES HEAT TREATMENT BERTINGKAT” Laporan Skripsi Teknik Mesin, Universitas Pancasakti Tegal 2021. Dalam kehidupan sehari-hari sampah merupakan benda yang dianggap sebagai barang yang tidak berguna, kotor dan menjijikan. Dalam mengatasi sebuah permasalah pencemaran akibat keberadaan sampah, diperlukan pengolahan dan penanganan sampah yang tentunya bisa bermanfaat untuk kita semua salah satunya adalah pengomposan. Dalam kemajuan bidangperindustrian tidak dapat dipisahkan dari perkembangan industri pisau atau pandai besi besar maupun kecil. Pada industri pembuatan pisau atau pandai besi sendiri mengalami beberapa permasalahan, diantaranya banyak konsumen yang mengeluhkan hasil ketajaman dan kekuatan dari pisau yang diproduksi. Terdapat beberapa faktor yang mempengaruhi ketajaman dan kekuatan pisau, diantaranya adalah media pendinginan pada saat proses perlakuan panas (Heat Treatment). Metode penelitian yang digunakana dalam metode eksperimen penelitian dengan menggunakan bahan baja ST 41. Proses pack carborizing menggunakan serbuk arang batok kelapa pada suhu 875℃ dengan media quenching air garam terhadap uji kekerasan dan uji keausan bahan. Nilai rata-rata dari pengujian kekerasan tertinggi terdapat pada pengujian carburising dan hardening memiliki kekerasan dengan nilai sebesar599,7 kg/mm2. Dan pengujian keausan tertinggi terdapat pada pengujian carburising, hardening dan tempering yaitu 0,000146 mm³/kg.m. Kata Kunci: Baja ST 41, Heat Treatment, Uji Kekerasan, Uji Keausan =============================================================================================== ABSTRACT MOHAMAD ABDUL JAELANI. 2021 "ANALYSIS OF ORGANIC WASTE CHARMING MACHINE USING ST 41 CARBON STEEL MATERIALS WITH LEVEL HEAT TREATMENT PROCESS" Thesis Report of Mechanical Engineering, University Pancasakti Tegal 2021. So far, waste has always been regarded as useless and disgusting goods. To solve the problem of pollution due to the presence of waste, one of which is composting and handling. The waste chopping machine is a tool that functions to facilitate chopping in accelerating the process of making organic waste into compost. In the industrial sector progress cannot be separated from the development of the knife industry or large and small blacksmiths. In the knife-making industry or blacksmiths themselves, they experience several problems, including many consumers who complain about the sharpness and strength of the knives that are produced. There are several factors that affect the sharpness and strength of the blades, including the cooling medium during the heat treatment process. The research method used is an experimental research method using ST 41 steel material. The pack carborizing process uses coconut shell charcoal powder at a temperature of 875℃ with salt water quenching media against the hardness test and the material wear test. The average value of the highest hardness testing is found in the carburising test and hardening has a hardness with a value of 599.7 kg / mm2. And the highest wear testing was found in the carburising, hardening and tempering tests, namely 0.000146 mm³ / kg.m. Keywords: Steel ST 41, heat treatment, hardness test, wear test.

Actions (login required)

View Item