PENGARUH VARIASI PENAMBAHAN FERO MANGAN (Fe-Mn) PADA SIFAT MEKANIS PENGECORAN BAJA KARBON RENDAH (AISI 1020)

BIL HAQUE, FAIQ RYAN (2025) PENGARUH VARIASI PENAMBAHAN FERO MANGAN (Fe-Mn) PADA SIFAT MEKANIS PENGECORAN BAJA KARBON RENDAH (AISI 1020). Skripsi thesis, Universitas Pancasakti Tegal.

	Text Cover_Bab 1 - 3 - Faiq Ryan Bil Haque.docx Download (3MB)
	Text BAB 4 - 5 - Faiq Ryan Bil Haque.docx Restricted to Repository staff only Download (118kB)
	Text DAFTAR PUSTAKA & Lampiran - Faiq Ryan Bil Haque.docx Download (5MB)

Abstract

Faiq Ryan Bil Haque, 2024 “Pengaruh Variasi Penambahan Fero Mangan (FeMn) Pada Sifat Mekanis Pengecoran Baja Karbon Rendah (AISI 1020)”. Laporan Skripsi Teknik Mesin Fakultas Teknik dan Ilmu Komputer Universitas PancaSakti Tegal 2024. Besi adalah elemen dasar sedangkan karbon adalah bahan paduan utama dalam baja, logam paduan. Selain karbon, unsur lain yang biasa ditambahkan ke paduan termasuk mangan, kromium, vanadium, dan tungsten. Mangan memiliki afinitas yang kuat terhadap oksigen dan dapat membentuk MnO yang stabil terhadap oksigen. Tujuan penelitian ini untuk mengetahui nilai kekerasan, tarik dan impak baja karbon rendah AISI 1020 setelah penambahan variasi ferromangan. Metode penelitian menggunakan alat: tungku induksi, timbangan digital, krusibel, tang penjepit dan thermocouple. Bahan yang digunakan: baja karbon rendah AISI 1020, feromangan dan bubuk kapur. Tungku induksi untuk melebur baja karbon rendah AISI 1020, ferromangan dengan kadar Mn 75%. Pada proses peleburan ini membutuhkan suhu diatas 1500C. Variasi yang digunakan penelitian ini adalah penambahan FeMn 1,5%, FeMn 2% dan FeMn 2,5%. Setelah melakukan pengecoran dan penambahan FeMn, spesimen akan diuji untuk mengetahui nilai kekerasan, kuat tarik dan harga impact. Hasil pengujian kekerasan penambahan FeMn 2,5% memiliki nilai rata-rata kekerasan paling tinggi dengan nilai kekerasan sebesar 436,6 BHN dan pengujian variasi penambahan FeMn 2% memiliki penurunan kekerasan sebesar 411,5 BHN. Sedangkan pada pengujian kekerasan dengan variasi penambahan 1,5% memiliki penurunan nilai yang sangat signifikan, sebesar 335,1 BHN. Sedangkan pada pengujian kuat tarik variasi penambahan FeMn 1,5% memiliki nilai rata-rata tegangan paling tinggi dari hasil pengujian. Variasi penambahan FeMn 1,5% memiliki nilai tegangan sebesar 320,2 MPa, sedangkan variasi penambahan FeMn 2% memiliki nilai tegangan sebesar 242,57 MPa dan variasi penambahan FeMn 2,5% memiliki nilai tegangan sebesar 256,19 MPa. Pada pengujian impact rata-rata pengujian impak pada Raw Material memiliki nilai 0,276 J/mm2 sedangkan pada variasi penambahan FeMn 1,5% sebesar 0.194 J/mm2, selanjutnya untuk pengecoran baja AISI 1020 dengan penambahan FeMn 2% diperoleh nilai rata-rata hasil pengujian impak sebesar 0,190 J/mm2 dan pengecoran baja AISI 1020 dengan penambahan FeMn 2,5% diperoleh nilai rata-rata hasil pengujian impak sebesar 0,167 J/mm2. Kata kunci: Besi, Peleburan Logam, Ferromangan, Sifat Mekanis Faiq Ryan Bil Haque, 2024 "The Effect of Variation of Ferro Manganese (FeMn) Addition on Mechanical Properties of Low Carbon Steel Casting (AISI 1020)". Mechanical Engineering Thesis Report, Faculty of Engineering and Computer Science, PancaSakti University, Tegal 2024. Iron is a basic element while carbon is the main alloying material in steel, alloy metals. In addition to carbon, other elements that are commonly added to alloys include manganese, chromium, vanadium, and tungsten. Manganese has a strong affinity for oxygen and can form MnO which is stable to oxygen. The purpose of this study was to determine the hardness, tensile and impact values of AISI 1020 low carbon steel after the addition of ferromanganese variations. The research method uses tools: induction furnace, digital scales, crucibles, pliers and thermocouple. Materials used: low carbon steel AISI 1020, ferromanganese and lime powder. Induction furnace for melting low carbon steel AISI 1020, ferromanganese with Mn content of 75%. This melting process requires a temperature above 1500C. The variations used in this study are the addition of FeMn 1.5%, FeMn 2% and FeMn 2.5%. After casting and adding FeMn, the specimen will be tested to determine the hardness value, tensile strength and impact price. The results of the hardness test of the addition of FeMn 2.5% have the highest average hardness value with a hardness value of 436.6 BHN and the test of the variation of the addition of FeMn 2% has a hardness decrease of 411.5 BHN. While in the hardness test with a variation of the addition of 1.5% there is a very significant decrease in value, amounting to 335.1 BHN. While in the tensile strength test, the variation of the addition of FeMn 1.5% has the highest average stress value from the test results. The variation of the addition of FeMn 1.5% has a stress value of 320.2 MPa, while the variation of the addition of FeMn 2% has a stress value of 242.57 MPa and the variation of the addition of FeMn 2.5% has a stress value of 256.19 MPa. In the impact test, the average impact test on the Raw Material has a value of 0.276 J/mm2 while the variation of the addition of FeMn 1.5% is 0.194 J/mm2, then for AISI 1020 steel casting with the addition of FeMn 2% the average value of the impact test results is 0.190 J/mm2 and AISI 1020 steel casting with the addition of FeMn 2.5% the average value of the impact test results is 0.167 J/mm2. Keywords: Iron, Metal Smelting, Ferromanganese, Mechanical Properties

Item Type:	Karya Ilmiah (Skripsi)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik dan Ilmu Komputer > Teknik Mesin
Depositing User:	admin repository upstegal
Date Deposited:	25 Feb 2025 02:41
Last Modified:	25 Feb 2025 02:41
URI:	http://repository.upstegal.ac.id/id/eprint/10172