ANALISA PENGUATAN MATA PISAU PENCACAH BOTOL PLASTIK MATERIAL BAJA KARBON RENDAH

ALTYASAFA, ANDRE FEBRIANSYACH (2025) ANALISA PENGUATAN MATA PISAU PENCACAH BOTOL PLASTIK MATERIAL BAJA KARBON RENDAH. Skripsi thesis, Universitas Pancasakti Tegal.

	Text SKRIPSI ANDRE COVER SAMPAI BAB 3.docx Download (9MB)
	Text SKRIPSI ANDRE BAB 4-5 - andre febriansyach.docx Restricted to Repository staff only Download (863kB)
	Text Daftar Pustaka-Lampiran skripsi andre - andre febriansyach.docx Download (1MB)

Abstract

ANDRE FEBRIANSYACH ALTYASAFA 2025 “ANALISA PENGUATAN MATA PISAU PENCACAH BOTOL PLASTIK MATERIAL BAJA KERBON RENDAH ” Laporan Skripsi Teknik Mesin. Universitas Pancasakti Tegal 2025. Dalam kehidupan sehari-hari yang dimana sampah merupakan benda yang sudah dibuang dan tidak terpakai lagi dengan kondisi yang kotor apabila sampah terus ada,maka sampah akan menjadi permasalahan serius di berbagai kota besar di Indonesia. Meningkatnya jumlah penduduk di Indonesia berbanding lurus dengan sampah yang dihasilkan tiap harinya. Sampah berdasarkan kandungan zat kimia dibagi menjadi dua kelompok, yaitu sampah organik dan anorganik salah satunya sampah botol plasik seiring dengan perkembangan ekonomi maka penggunaan plastik akan semakin banyak dan menjadi masalah di lingkungan karena sulit terurai. Oleh karena itu untuk mengurangi sampah botol plastik tersebut di cacah menggukanan mesin pencacah botol plastik. Hal tersebut dapat mengurangi permasalahan sampah yang sudah ada disekitar kita. Dengan adanya kemajuan teknologi seperti sekarang ini mulai dikembangkan alternatif dalam menangani sampah botol plastik ini. Akan tetapi banyak mesin pencacah yang mengalami kerusakan pada mata pisaunya untuk itu penelitian ini Bertujuan untuk memperbaiki sifat fisik dan mekanik pisau untuk membuat mata pisau pencacah botol plastik dan untuk mengatahui kualitas pada ketajaman dan kekuatan pisau pada mesin pencacah tersebut apakah akan mengalami penurunan atau cepat tumpul. Metode penelitian yang penulis gunakan dalam penelitian ini adalah metode eksperimen Pada metode penelitian ini menggunakan baja ST 41, yang digunakan di pack carburizing melnggulnakan arang batok kellapa delngan sulhul 800°C,850°C, 900°C. setelah itu di quenching dengan media pendinginan air garam terhadap Uji Kekerasan, Uji Kaeusan dan Uji Impact. Nilai rata-rata dari pengujian kekerasan tertinggi terhadap pada pengujian Carburizing dengan variasi suhu memiliki kekerasan sebesar 392,0 kg/mm2. pengujian keausan tertingii terdapat pada pengujin Carburuzing dengan variasi suhu sebesar 0,000433 mm3/kg.m. Dan pengujian impact tertinggi terhadap pada pengujian Carburizing dengan variasi suhu sebesar 3,180 J/mm²,. Kata Kunci : Baja ST 41, Heat Treatment , Uji Kekerasan, Uji Keausan, Uji Impact . ABSTRACT ANDRE FEBRIANSYACH ALTYASAFA 2025 "ANALYSIS OF STRENGTHENING BLADES FOR PLASTIC BOTTLE CRASHERS IN LOW CARBON STEEL MATERIALS" Mechanical Engineering Thesis Report. Pancasakti University Tegal 2025. In everyday life, where rubbish is objects that have been thrown away and are no longer used and are in dirty conditions, if rubbish continues to exist, rubbish will become a serious problem in various big cities in Indonesia. The increase in population in Indonesia is directly proportional to the waste produced every day. Waste based on chemical content is divided into two groups, namely organic and inorganic waste, one of which is plastic bottle waste. Along with economic development, the use of plastic will increase and become a problem in the environment because it is difficult to decompose. Therefore, to reduce waste, plastic bottles are chopped using a plastic bottle chopper machine. This can reduce the waste problem that already exists around us. With advances in technology such as today, alternatives are starting to be developed for dealing with plastic bottle waste. However, many chopping machines experience damage to their blades, so this research aims to improve the physical and mechanical properties of knives to make plastic bottle chopping blades and to find out whether the quality of the sharpness and strength of the blades on these chopping machines will decrease or become dull quickly. The research method that the author uses in this research is the experimental method. This research method uses ST 41 steel, which is used in pack carburizing using coconut shell charcoal with sulhul 800°C, 850°C, 900°C. after that it is quenched with salt water cooling media for Hardness Test, Wear Test and Impact Test. The average value of the highest hardness test in the Carburizing test with temperature variations has a hardness of 392.0 kg/mm2. The highest wear test was found on the Carburuzing tester with a temperature variation of 0.000433 mm3/kg.m. And the highest impact test was carried out in the Carburizing test with a temperature variation of 3,180 J/mm². Keywords: ST 41 Steel, Heat Treatment, Hardness Test, Wear Test, Impact Test.

Item Type:	Karya Ilmiah (Skripsi)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik dan Ilmu Komputer > Teknik Mesin
Depositing User:	admin repository upstegal
Date Deposited:	13 Mar 2025 02:15
Last Modified:	13 Mar 2025 02:15
URI:	http://repository.upstegal.ac.id/id/eprint/10272

Actions (login required)

View Item