PENGARUH VARIASI SUHU TUANG TERHADAP KEKUATAN PENGECORAN LOGAM ALUMINIUM PADUAN DALAM PEMBUATAN JENDELA KAPAL

SETIO PRATAMA, MUHAMMAD FADEL (2025) PENGARUH VARIASI SUHU TUANG TERHADAP KEKUATAN PENGECORAN LOGAM ALUMINIUM PADUAN DALAM PEMBUATAN JENDELA KAPAL. Skripsi thesis, Universitas Pancasakti Tegal.

	Text cover bab 3 M.Fadel.pdf Download (1MB)
	Text BAB 4 - 5 BABEHHH - Muhammad fadel Setio.docx Restricted to Repository staff only Download (858kB)
	Text DAFTAR PUSTAKA - lampiran - Muhammad fadel Setio.docx Download (3MB)

Abstract

Kekuatan dan komposisi paduan alumunium harus diuji dengan baik. Dalam pembuatan komponen komponen kapal harus memiliki spesifikasi teknis dari pengguna. Dalam penelitian ini menggunakan metode eksperimen dengan memaparkan secara jelas hasil eksperimen terhadap benda uji, kemudian hasil analisis datanya didasarkan pada angka-angka hasil perhitungan uji makro struktur, uji kekerasan dan uji tarik. Dapat disimpulkan sebagai berikut : Pada hasil pengujian Kekerasan Vickers, saat uji variasi specimen 700º memiliki nilai ratarata sebesar 71,4 VHN. Pada saat variasi specimen 750º memiliki hasil nilai ratarata 73,6º VHN, kemudian pada uji specimen menggunakan 800º memiliki hasil rata-rata sebesar 72,0 VHN. Maka semakin kuat kekerasan yang dihasilkan pada specimen tersebut. Hasil nilai Uji Tarik pada specimen variasi suhu 700º mempunyai nilai rata-rata sebesar 83,2 Mpa, kemudian pada variasi specimen uji 750º menghasilkan nilai rata-rata 83,4 Mpa, lalu pada saat pengujian specimen variasi suhu 800º menghasilkan nilai rata-rata sebesar 80,6 Mpa. Hal ini menunjukan pada saat variasi suhu 750º memiliki nilai tinggi, Pada hasil uji Korosi menunjukan bahwa laju korosi dengan variasi suhu 700º mempunyai nilai rata-rata 0,042 mm/years, kamudian pada variasi suhu 750º memiliki nilai rata-rata sebesar 0,120 mm/years, dan pada variasi suhu 800º mempunyai nilai rata-rata 0,63. Hal ini disimpulkan bahwa semakin kecil variasi suhu yang diujikan maka semakin kecil pula tingkat kekorosian yang dihasilkan oleh specimennya pada variasi suhu 700º yang mempnyai nilai 0,042 mm/years. Kata Kunci : Aluminium, uji Tarik, Kekerasan, Korosi, Mg The strength and composition of aluminum alloys should be well tested. In the manufacture of components, ship components must have technical specifications from the user. In this study, an experimental method is used by clearly explaining the results of the experiment on the test object, then the results of the data analysis are based on the results of the calculation of the macro structural test, hardness test and tensile test. It can be concluded as follows: In the Vickers Hardness test results, when the specimen variation test of 700º has an average value of 71.4 VHN. When the variation of the 750º specimen had an average result of 73.6º VHN, then in the specimen test using 800º had an average result of 72.0 VHN. So the stronger the hardness produced on the specimen. The results of the Tensile Test value on the 700º temperature variation specimen have an average value of 83.2 Mpa, then the 750º test specimen variation produces an average value of 83.4 Mpa then at the time of testing the specimen the temperature variation of 800º produced an average value of 80.6 Mpa. This shows that when the temperature variation of 750º has a high value, the results of the Corrosion test show that the corrosion rate with a temperature variation of 700º has an average value of 0.042 mm/years, the temperature variation of 750º has an average value of 0.120 mm/years, and at the temperature variation of 800º has an average value of 0.63. It is concluded that the smaller the temperature variation tested, the smaller the corrosion level produced by the specimen at a temperature variation of 700º which has a value of 0.042 mm/years. Keywords : Aluminum, Tensile test, Hardness, Corrosion, Mg

Item Type:	Karya Ilmiah (Skripsi)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik dan Ilmu Komputer > Teknik Mesin
Depositing User:	admin repository upstegal
Date Deposited:	21 Mar 2025 02:36
Last Modified:	21 Mar 2025 02:36
URI:	http://repository.upstegal.ac.id/id/eprint/10334

Actions (login required)

View Item